Preparation of TiO2/Ti mesh photoelectrode and properties

An innovative photoelectrode, TiO2/Ti mesh electrode, was prepared by anodisation. In anodisation, 0.5 mol/L H2SO4 was sued as electrolytic solution, the current had been constantly 1A from the beginning of the oxidation until reaching a designed voltage. Results showed that the photocatalytic activity of electrode was better when the designed voltage was 160V. The morphology and the crystalline texture of the TiO2 film on mesh electrode were examined by scanning electronic microscopy and Raman spectroscopy respectively. The examination results indicated that the structure and properties of the film depended on anodisation rate, and the anatase was the dominant component under the controlled experimental conditions. Degradation of Rhodamine B in photocatalytic (PC) and photoelectrocatalytic (PEC) reaction was investigated.

作 者： LIU Hui-ling LI Xuan-dong ZHOU Ding LI Xiang-zhong YUE Ping-tao   作者單位： LIU Hui-ling,LI Xuan-dong,ZHOU Ding(Department of Environmental Engineering, Harbin Institute of Technology, Harbin 150001, China)

LI Xiang-zhong,YUE Ping-tao(Department of Civil and Structural Engineering, The Hong Kong Polytechnic University, Hung Hom, Komloon, Hong Kong) 

刊 名： 環(huán)境科學學報(英文版)  ISTIC SCI 英文刊名： JOURNAL OF ENVIRONMENTAL SCIENCES  年，卷(期)： 2003 15(3)  分類號： X13  關鍵詞： mesh photoelectrode   anodisation   TiO2   photoelectrocatalytic oxidation   rhodamine B  

【Preparation of TiO2/Ti mesh photoele】相關文章：

雙元Ti載體的發(fā)展04-26

Preparation of TiO2-activated carbon complex membranes and their photoelectrocatalytic activity04-27

Preparation and Characterization of Refuse Derived Fuel for Pyrolysis and Gasification by Bindless High Pressure Briquet04-26

高度分散TiO2催化超聲降解乙基紫及與懸浮TiO2催化活性的比較04-25

Preparation and characterization of mixed hydroxy-Fe-Al pillared montmorillonite with large basal spacing04-26

納米TiO2治理室內甲醛的實驗研究04-25

Pt/TiO2對水中黑索今的光催化降解04-26

金紅石型納米TiO2的制備04-27

Electro-catalytic oxidation of phenol with Ti-base lead dioxide electrode04-27

Preparation and mechanism of Fe3O4/Au core/shell super-paramagnetic microspheres04-26